| Manufacturer | Polymaker | |
| Product Name | Fiberon PA612-CF15 | |
| Filament Type | PA612 | |
| Finish | Carbon Fiber |
| Nozzle Temperature | 250-300 °C | |
| Bed Temperature | 40-50 °C | |
| Print Speed | 300 mm/s | |
| Cooling Fan | OFF |
| Density | 1.03 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 9.9 g/10 min | 260 °C, 2.16 kg |
| Melting temperature | 210 °C | DSC, 10 °C/min |
| Crystallization temperature | 180 °C | DSC, 10 °C/min |
| Decomposition temperature | 448.4 °C | TGA, 20 °C/min |
| Vicat softening temperature | 206.2 °C | ISO 306, GB/T 1633 |
| Heat deflection temperature (1.8 MPa) | 114 °C | ISO 75 |
| Heat deflection temperature (0.45 MPa) | 175 °C | ISO 75 |
| Young's modulus (X-Y) | 5136.7 MPa ±192.2 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 2786.4 MPa ±78.4 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 91.9 MPa ±2 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 48.3 MPa ±3.9 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 2.6 % ±0.2 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 2.1 % ±0.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 4583.5 MPa ±62.7 | ISO 178, GB/T 9341 |
| Bending modulus (Z) | 2264.8 MPa ±203.8 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 138 MPa ±2.2 | ISO 178, GB/T 9341 |
| Bending strength (Z) | 73.5 MPa ±3.9 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) | 8.1 kJ/m² ±0.8 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) | 29.9 kJ/m² ±1.6 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) | 12.6 kJ/m² ±1.4 | ISO 179, GB/T 1043 |
| Young's modulus (X-Y) (moisture conditioned) | 3990.8 MPa ±136.5 | ISO 527, GB/T 1040 |
| Young's modulus (Z) (moisture conditioned) | 2386.8 MPa ±150.2 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) (moisture conditioned) | 83.1 MPa ±2.2 | ISO 527, GB/T 1040 |
| Tensile strength (Z) (moisture conditioned) | 35.6 MPa ±3 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) (moisture conditioned) | 4.1 % ±0.3 | ISO 527, GB/T 1040 |
| Elongation at break (Z) (moisture conditioned) | 1.7 % ±0.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) (moisture conditioned) | 3888.3 MPa ±56.3 | ISO 178, GB/T 9341 |
| Bending modulus (Z) (moisture conditioned) | 1764.5 MPa ±98.9 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) (moisture conditioned) | 118.1 MPa ±1.6 | ISO 178, GB/T 9341 |
| Bending strength (Z) (moisture conditioned) | 64.6 MPa ±2 | ISO 178, GB/T 9341 |
| Notched Charpy impact strength (X-Y) (moisture conditioned) | 7.7 kJ/m² ±0.5 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (X-Y) (moisture conditioned) | 41 kJ/m² ±1.4 | ISO 179, GB/T 1043 |
| Un-notched Charpy impact strength (Z) (moisture conditioned) | 17.6 kJ/m² ±2 | ISO 179, GB/T 1043 |
| Flame retardancy | HB | Data Sheet |
| Technical Data Sheet | View Data Sheet | Version 1.1 · 2024-12 |
| Fiberon PA612-CF15 TDS page on wiki.polymaker.com | Open link | |