Polymaker Fiberon PA612-CF15 Black

Latest price$34.99$69.98 per kg

Buy on Amazon →

Manufacturer	Polymaker
Filament type	PA612
Data sheet	Not available
Format	-
Finish	Carbon Fiber
Color	Black
Warranty	No info provided
Availability	In Stock
Image	Polymaker Fiberon PA612-CF15 Carbon Fiber Nylon Filament 1.75mm, Black, 0.5kg

Technical properties

CompareVisualize

Density	1.03 g/cm³	ISO 1183, GB/T 1033
Melt index	9.9 g/10 min	260 °C, 2.16 kg
Melting temperature	210 °C	DSC, 10 °C/min
Crystallization temperature	180 °C	DSC, 10 °C/min
Decomposition temperature	448.4 °C	TGA, 20 °C/min
Vicat softening temperature	206.2 °C	ISO 306, GB/T 1633
Young's modulus (X-Y)	5136.7 MPa ±192.2	ISO 527, GB/T 1040
Young's modulus (Z)	2786.4 MPa ±78.4	ISO 527, GB/T 1040
Tensile strength (X-Y)	91.9 MPa ±2	ISO 527, GB/T 1040
Tensile strength (Z)	48.3 MPa ±3.9	ISO 527, GB/T 1040
Elongation at break (X-Y)	2.6 % ±0.2	ISO 527, GB/T 1040
Elongation at break (Z)	2.1 % ±0.2	ISO 527, GB/T 1040
Bending modulus (X-Y)	4583.5 MPa ±62.7	ISO 178, GB/T 9341
Bending modulus (Z)	2264.8 MPa ±203.8	ISO 178, GB/T 9341
Bending strength (X-Y)	138 MPa ±2.2	ISO 178, GB/T 9341
Bending strength (Z)	73.5 MPa ±3.9	ISO 178, GB/T 9341
Notched Charpy impact strength (X-Y)	8.1 kJ/m² ±0.8	ISO 179, GB/T 1043

Characteristics

Flame retardancy

HB

Data Sheet

Print suggestions

Nozzle temp	250-300 °C
Print speed	300 mm/s
Build surface temp	40-50 °C
Drying temperature	100 °C
Drying time	10 hours
Enclosed chamber	Room temperature
Annealing temperature	100 °C
Annealing time	16 hours
Cooling fan	OFF