| Manufacturer | Polymaker |
| Filament type | ASA |
| Data sheet | Not available |
| Format | - |
| Finish | Carbon Fiber |
| Color | |
| Warranty | No info provided |
| Availability | In Stock |
| Image |  Polymaker Fiberon ASA-CF08 Carbon Fiber ASA Filament 1.75mm, Dark Grey, 0.5kg |
| Density | 1.09 g/cm³ | ISO 1183, GB/T 1033 |
| Melt index | 13.9 g/10 min | 240 °C, 5 kg |
| Glass transition temperature | 106.6 °C | DSC, 10 °C/min |
| Decomposition temperature | 328.4 °C | TGA, 20 °C/min |
| Vicat softening temperature | 110.8 °C | ISO 306, GB/T 1633 |
| Young's modulus (X-Y) | 3611.7 MPa ±181.1 | ISO 527, GB/T 1040 |
| Young's modulus (Z) | 1903.8 MPa ±71 | ISO 527, GB/T 1040 |
| Tensile strength (X-Y) | 43.5 MPa ±0.7 | ISO 527, GB/T 1040 |
| Tensile strength (Z) | 25 MPa ±0.4 | ISO 527, GB/T 1040 |
| Elongation at break (X-Y) | 1.8 % ±0.1 | ISO 527, GB/T 1040 |
| Elongation at break (Z) | 2.7 % ±0.2 | ISO 527, GB/T 1040 |
| Bending modulus (X-Y) | 3265 MPa ±56.5 | ISO 178, GB/T 9341 |
| Bending modulus (Z) | 1743.4 MPa ±59.9 | ISO 178, GB/T 9341 |
| Bending strength (X-Y) | 69.1 MPa ±1.62 | ISO 306, GB/T 1633 |
| Bending strength (Z) | 46.5 MPa ±0.8 | ISO 306, GB/T 1633 |
| Notched Charpy impact strength (X-Y) | 5.5 kJ/m² ±0.14 | ISO 179, GB/T 1043 |
Characteristics
| Flame retardancy | HB | Data Sheet |
Print suggestions
| Nozzle temp | 260-280 °C |
| Print speed | 350 mm/s |
| Build surface temp | 90-100 °C |
| Drying temperature | 90 °C |
| Drying time | 6 hours |
| Enclosed chamber | Room temp. |
| Cooling fan | OFF |