Polymaker Fiberon PA12-CF10 Black

Latest priceUnavailable

Buy on Amazon →

Manufacturer	Polymaker
Filament type	PA12
Data sheet	Not available
Format	-
Finish	Carbon Fiber
Color	Black Available in 4 other colors →
Warranty	No info provided
Availability	API Error: 403
Image	Polymaker Fiberon PA612-CF15 Carbon Fiber Nylon Filament 1.75mm, Black, 0.5kg

Technical properties

CompareVisualize

Density	1.06 g/cm³	ISO 1183, GB/T 1033
Melt index	25 g/10 min	280 °C, 2.16 kg
Glass transition temperature	55 °C	DSC, 10 °C/min
Melting temperature	171 °C	DSC, 10 °C/min
Crystallization temperature	120 °C	DSC, 10 °C/min
Decomposition temperature	445.2 °C	TGA, 20 °C/min
Vicat softening temperature	170.2 °C	ISO 306, GB/T 1633
Young's modulus (X-Y)	3311.2 MPa ±134.9	ISO 527, GB/T 1040
Young's modulus (Z)	1806.6 MPa ±145.7	ISO 527, GB/T 1040
Tensile strength (X-Y)	77.4 MPa ±1.1	ISO 527, GB/T 1040
Tensile strength (Z)	52.2 MPa ±0.8	ISO 527, GB/T 1040
Elongation at break (X-Y)	4.2 % ±0.4	ISO 527, GB/T 1040
Elongation at break (Z)	5 % ±1	ISO 527, GB/T 1040
Bending modulus (X-Y)	2886.5 MPa ±144.8	ISO 178, GB/T 9341
Bending modulus (Z)	1452.8 MPa ±96.5	ISO 178, GB/T 9341
Bending strength (X-Y)	112.4 MPa ±1	ISO 178, GB/T 9341
Bending strength (Z)	69.8 MPa ±2.2	ISO 178, GB/T 9341
Notched Charpy impact strength (X-Y)	9.9 kJ/m² ±0.7	ISO 179, GB/T 1043

Characteristics

Flame retardancy

HB

Data Sheet

Print suggestions

Nozzle temp	280-300 °C
Print speed	300 mm/s
Build surface temp	40-50 °C
Drying temperature	100 °C
Drying time	10 hours
Enclosed chamber	Room temperature
Annealing temperature	100 °C
Annealing time	16 hours
Cooling fan	OFF