Polymaker PC-ABS, Black
Latest price$42.49$42.49 per kg
Buy on Amazon →| Manufacturer | Polymaker |
| Filament type | PC-ABS |
| Data sheet | Not available |
| Format | 1.75-2.85 mm ±0.03 |
| Finish | Blend |
| Color | Black Available in 1 other colors → |
| Warranty | No info provided |
| Availability | Only 10 left in stock - order soon. |
| Image |  Polymaker PC-ABS Filament 2.85mm, Black Polycarbonate Blend with ABS 1kg - Tough and Heat Resistant 2.85mm 3D Printer Polycarbonate Filament, Dimensional Accuracy +/- 0.03mm |
Technical properties
| Density | 1.1 g/cm³ | ISO 1183 |
| Glass Transition Temperature | 108 °C | DSC, 10°C/min |
| Vicat Softening Temperature | 112 °C | ISO 306 |
| Melt Index | 10 g/10 min | 260°C, 2.16kg |
| Young's Modulus (X-Y) | 2152 MPa ±63 | ISO 527 |
| Young's Modulus (Z) | 1821 MPa ±179 | ISO 527 |
| Tensile Strength (X-Y) | 42.29 MPa ±1.17 | ISO 527 |
| Tensile Strength (Z) | 30.92 MPa ±1.85 | ISO 527 |
| Elongation at Break (X-Y) | 2.6 % ±0.36 | ISO 527 |
| Elongation at Break (Z) | 2.23 % ±0.29 | ISO 527 |
| Flexural Modulus (X-Y) | 2068 MPa ±45 | ISO 178 |
| Flexural Strength (X-Y) | 69.29 MPa ±2.15 | ISO 178 |
| Charpy Impact Strength (X-Y) | 27.8 kJ/m² ±1.79 | ISO 179 |
Characteristics
| Effect of Weak Acids | Good | Source → |
| Effect of Weak Alkalis | Fair | Source → |
| Effect of Oils & Grease | Good | Source → |
| Effect of Strong Acids | Poor | Source → |
| Effect of Strong Alkalis | Poor | Source → |
Print suggestions
| Nozzle temp | 260-280 °C |
| Build surface material | Glass, PEI |
| Build surface treatment | None |
| Build surface temp | 90-110 °C |
| Cooling fan | Off |
| Print speed | 30-60 mm/s |
| Retraction distance | 3-6 mm |
| Retraction speed | 40-60 mm/s |
| Drying temperature | 80 °C |
| Drying time | 12 h |
| Annealing temperature | 105 °C |
| Annealing time | 6 h |
| Chamber temperature | 70-100 °C |