Polymaker Fiberon PA6-GF25 Grey

Latest priceUnavailable

Buy on Amazon →

Manufacturer	Polymaker
Filament type	PA6
Data sheet	Not available
Format	-
Finish	Glass Fiber
Color	Grey Available in 1 other colors →
Warranty	No info provided
Availability	API Error: 403
Image	Polymaker Fiberon PA6-GF25 Glass Fiber Nylon Filament 1.75mm, Grey, 0.5kg

Technical properties

CompareVisualize

Density	1.2 g/cm³	ISO 1183, GB/T 1033
Melt index	15.9 g/10 min	300 °C, 2.16 kg
Glass transition temperature	70.4 °C	DSC, 10 °C/min
Melting temperature	214.5 °C	DSC, 10 °C/min
Crystallization temperature	174.5 °C	DSC, 10 °C/min
Decomposition temperature	437.1 °C	TGA, 20 °C/min
Vicat softening temperature	211.7 °C	ISO 306, GB/T 1633
Young's modulus (X-Y)	5356.9 MPa ±211	ISO 527, GB/T 1040
Young's modulus (Z)	3375.9 MPa ±142.1	ISO 527, GB/T 1040
Tensile strength (X-Y)	80.1 MPa ±1.8	ISO 527, GB/T 1040
Tensile strength (Z)	60.7 MPa ±1.1	ISO 527, GB/T 1040
Elongation at break (X-Y)	2.4 % ±0.2	ISO 527, GB/T 1040
Elongation at break (Z)	4 % ±0.4	ISO 527, GB/T 1040
Bending modulus (X-Y)	4314.2 MPa ±120.6	ISO 178, GB/T 9341
Bending modulus (Z)	2849.5 MPa ±282.1	ISO 178, GB/T 9341
Bending strength (X-Y)	133.8 MPa ±4.7	ISO 178, GB/T 9341
Bending strength (Z)	99.9 MPa ±3.2	ISO 178, GB/T 9341
Notched Charpy impact strength (X-Y)	10 kJ/m² ±0.7	ISO 179, GB/T 1043

Characteristics

Flame retardancy

HB

Data Sheet

Print suggestions

Nozzle temp	280-300 °C
Print speed	300 mm/s
Build surface temp	40-50 °C
Drying temperature	100 °C
Drying time	10 hours
Enclosed chamber	Room temperature
Annealing temperature	100 °C
Annealing time	16 hours
Cooling fan	OFF