Polymaker Fiberon PA6-CF20, Black
Latest price$35.99$71.98 per kg
Buy on Amazon →| Manufacturer | Polymaker |
| Filament type | PA6 |
| Data sheet | Not available |
| Format | 1.75-2.85 mm ±0.03 |
| Finish | Carbon Fiber |
| Color | Black Available in 2 other colors → |
| Warranty | No info provided |
| Availability | In Stock |
| Image |  Polymaker Fiberon PA6-CF Carbon Fiber Nylon Filament 1.75mm Black 0.5kg, Fiberon PA6-CF Nylon Warp Free 1.75mm 3D Printing Filament |
Technical properties
| Density | 1.17 g/cm³ | ISO 1183 |
| Glass Transition Temperature | 74.2 °C | DSC |
| Melting Temperature | 218.5 °C | DSC |
| Crystallization Temperature | 184.6 °C | DSC |
| Decomposition Temperature | 370 °C | TGA |
| Young's Modulus (X-Y) - Annealed | 7453 MPa ±656 | ISO 527 |
| Young's Modulus (Z) - Annealed | 4354 MPa ±206 | ISO 527 |
| Tensile Strength (X-Y) - Annealed | 105 MPa ±5 | ISO 527 |
| Tensile Strength (Z) - Annealed | 67.7 MPa ±4.7 | ISO 527 |
| Elongation at Break (X-Y) - Annealed | 3 % ±0.3 | ISO 527 |
| Elongation at Break (Z) - Annealed | 2.5 % ±0.7 | ISO 527 |
| Bending Modulus (X-Y) - Annealed | 8339 MPa ±369 | ISO 178 |
| Bending Strength (X-Y) - Annealed | 169 MPa ±4.7 | ISO 178 |
| Charpy Impact Strength (X-Y) - Annealed | 13.34 kJ/m² ±0.5 | ISO 179 |
Print suggestions
| Nozzle temp | 280-300 °C |
| Build surface material | Glass, PEI |
| Build surface treatment | None |
| Build surface temp | 25-50 °C |
| Cooling fan | Off |
| Print speed | 30-60 mm/s |
| Retraction distance | 3 mm |
| Retraction speed | 40 mm/s |
| Drying temperature | 80 °C |
| Drying time | 6 h |
| Annealing temperature | 80-100 °C |
| Annealing time | 6 h |